Tubular positive plates: Our tubular positive grids are produced in state of art pressure.die casting machines. Due to this facility which is rare amongst S.S.I. Units, we are
In a position to manufacture these grids with special low antimony selenium hybrid alloy that are free from blow holes, have dense uniform grain structure, high mechanical strength and good dimensional accuracy. The active material is manufactured in house using virgin lead. This active material is encapsulated in between the grid and pluri tubular bag which snugly fits on the grid and the open end is sealed with plastic bottom bars. This construction retains the active material intact and prevents shedding of active material during long service life of the battery.

Negative Plates : The negative plates are of pasted type with sturdy grids and the active material is a blend of oxide, special additives/binders and expanders which aids in better voltage build up and charging characteristics.

Separators: Imported Industrial grade Polyethylene Separators are used. These separators are laser tested for detecting pin holes, they have good mechanical strength , Porocity and low Electrical resistance

Aqua trap vent plugs   : R.D.S.O. Approved aqua trap vent plugs  are used. These Vent plugs  prevent the electrolyte loss during  charging of the battery.

P.P Battery Case  :  Batteries are assembled in  Polypropylene containers which imparts aesthetic look to the batteries.  Intercell  connection  is established  by fusion electrical resistance welding process.



Use of hybrid alloy and pressure die-casting process coupled with high purity of
Active materials used:

  • Enhances the life of the Battery, prevents leaching of antimony into the Electrolyte whereby self discharge is minimum.
  • Renders low maintenance characteristics to the battery and hence less topping up.
  • Builds adequate back emf and resists over charging. This protects the charging system apart from savings on electricity.
  • Increases life span of the battery.


Use of special additives and expanders in the negative paste formulation:

  • Renders the batteries suitable for deep discharge applications.
  • Renders the batteries suitable for deep discharge applications.
  • Prevents negative growth.
  • Improves terminal voltage..


Use of Poly-ethylene separators have several advantages:

  • As they have good mechanical strength and are free from pin holes chances of failure of battery on this account is not there.
  • Since Poly-ethylene Separators have High Porocity & Low Electrical Resistance, the voltage drop across the terminals when the battery is on load is less.
  • Reduces temperature build up inside the battery .
  • Increases power output from the battery.


Aqua trap vent plugs:

  • Prevents electrolyte loss during the charging process by trapping the acid mist.
  • The surrounding atmosphere will be free from acid fumes.
  • Reduces the topping up frequency.


Since polypropylene containers are us:

  • The batteries are much lighter and attractive.
  • There is no sweating of the electrolyte.
  • Easy to clean and maintain.


Through partition Intercell connection :

  • Reduce intercell resistance of the battery.
  • Prevents heating up of battery while charging and discharging.
  • No loose contacts within the battery.



  • For initial charging, follow instructions printed on the battery.
  • Install the batteries on an insulated surface such as a sheet of Rubber or Wooden Plank.
  • Electrical connections should be secure to prevent sparkling & melting of terminals.
  • Take care not to offer much load on terminals while tightening.
  • Take care not to short circuit the terminals while tightening.
  • Apply white petroleum jelly to the terminals to prevent corrosion.
  • Batteries should be installed in well ventilated place sheltered from sunlight.
  • Do not bring fire hazardous material, flame, lighted cigarettes near to the battery as there is chance of explosion or injury.
  • Keep the surface of the battery clean & tidy.
  • Check the electrolyte level periodically & top up with distilled water only if required. Never use acid to top up.